SABIC Innovative Plastics LNP LUBRICOMP DI001L PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DI001L PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* DI001L is a compound based on Polycarbonate resin containing 2% Silicone. Added characteristics of this grade are: Low Extractable.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ASTM D792
Moisture Absorption	0.170 %	0.170 %	50% RH, 24 hrs; ASTM D570
	0.220 %	0.220 %	23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Time 86400 sec	0.0050 - 0.0080 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 - 0.010 cm/cm @Time 86400 sec	0.0070 - 0.010 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	Type I, 5 mm/min; ASTM D638
	48.0 MPa	6960 psi	5 mm/min; ISO 527
Tensile Strength, Yield	57.0 MPa	8270 psi	5 mm/min; ISO 527
	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	42.8 %	42.8 %	5 mm/min; ISO 527
	49 %	49 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	6.3 %	6.3 %	5 mm/min; ISO 527
	6.6 %	6.6 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	2.21 GPa	321 ksi	1 mm/min; ISO 527
	2.28 GPa	331 ksi	50 mm/min; ASTM D638
Flexural Strength	72.0 MPa	10400 psi	ISO 178
Flexural Modulus	2.11 GPa	306 ksi	2 mm/min; ISO 178
	2.36 GPa	342 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	7.82 J/cm	14.7 ft-lb/in	ASTM D256
Izod Impact, Unnotched	20.6 J/cm	38.6 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	62.0 kJ/m²	29.5 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	179 kJ/m²	85.2 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	41.0 J @Temperature 23.0 °C	30.2 ft-lb @Temperature 73.4 °F	ASTM D3763
Impact Test	48.0 J	35.4 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.16	0.16	ASTM D3702 Modified
Coefficient of Friction, Static	0.18	0.18	ASTM D3702 Modified
K (wear) Factor	876 x 10^-8 mm³/N-M	435 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	57.0 µm/m-°C @Temperature -30.0 - 30.0 °C	31.7 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM D696
CTE, linear, Transverse to Flow	68.0 µm/m-°C @Temperature -30.0 - 30.0 °C	37.8 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	141 °C	286 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	141 °C @Thickness 3.20 mm	286 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	127 °C	261 °F	Flatw 80104 sp=64mm; ISO 75/Af
	128 °C @Thickness 3.20 mm	262 °F @Thickness 0.126 in	unannealed; ASTM D648