- Polymer Property : Flexural Modulus = 2.36 GPa
Polymer Property : Flexural Modulus = 2.36 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® 123X PC Copolymer Improved flow PC with excellent processability and mold release. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® 123X PC Copolymer (Europe-Africa-Middle East) Improved flow PC with excellent processability and mold release.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® BPL1000 PC Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® BPL1000 PC (Europe-Africa-Middle East) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® FXM173R PC UV stabilized PC in special effects colors. Metallic and pearlescent additives. Color may affect performance.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DI001L PC LNP* LUBRICOMP* DI001L is a compound based on Polycarbonate resin containing 2% Silicone. Added characteristics of this grade are: Low Extractable. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® 143X PC Copolymer (Asia Pacific) Improved flow PC with excellent processability and mold release. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRILOY UX99725 PPA LNP LUBRILOY* UX99725 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Flexural Modulus | 2.36 GPa | 343 ksi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant Scratch resistant material that is used for the exterior material of flat TVInformation provided by Samsung Cheil Industries. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL LS6010 PPE+HIPS Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Asia Pacific) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL NH6010B PPE+HIPS Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL PVX516 PPE PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT |
|||
| Flexural Modulus | 2.36 GPa | 343 ksi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant Scratch resistant material that is used for the exterior material of flat TVInformation provided by Samsung Cheil Industries. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific) High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PA (Asia Pacific) High flow PPE+PA for under-the-hood and electrical applications. With mold release |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PS+PA High flow PPE+PS+PA for under-the-hood and electrical applications. With mold release |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific) High flow PPE+PS+PA for under-the-hood and electrical applications. With mold releaseThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | ISO 178 |
| Lubrizol ESTALOC® 59200 Ester-Type, Reinforced Engineering Thermoplastic (European Grade) Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio.. |
|||
| Flexural Modulus | 2.36 - 2.48 GPa | 342 - 360 ksi | ASTM D790M |
| DSM Somos® ProtoGen™ O-XT 18120 Epoxy Resin for Stereolithography, UV Postcure at HOC -2 DescriptionDSM Somos® ProtoGen O-XT 18120 is a liquid photopolymer that produces accurate parts ideal for general purpose applications. ProtoGen resins are the first SL resins to demonstrate diffe.. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | tangent; chs 0.05 in/min; ASTM D790 |
| Diamond Polymers ABS 3501ELG High Impact, Low Gloss Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Flexural Modulus | 2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® 123X PC Copolymer (Asia Pacific) Improved flow PC with excellent processability and mold release. |
|||