Resinlab® CYNERGY CA6008 Adhesive

Category Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer Resinlab®
Trade Name CYNERGY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® CYNERGY CA6008 Adhesive.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Description: The CYNERGY 6000 SERIES are for use in demanding applications where very fast cure speeds are required. These are single component solvent free materials manufactured in a wide variety of viscosities and setting times to satisfy specific bonding applications. Substrates such a wood, plastics, metal, rubber, or other materials are bonded quickly and effectively with the Cynergy 6000 series. These products are less dependent on surface moisture for achieving cure speed than most standard grades of cyanoacrylates.Application: The CYNERGY SERIES of the cyanoacrylates should be applied in small amounts to one surface only. The parts should then be mated together under slight pressure. This causes the adhesive to spread out into a thin film and assures optimum adhesive performance. The pressure need only be applied for several seconds. The CYNERGY SERIES cures rapidly allowing for bonded parts to be handled within 10 to 60 seconds for most applications. Full cure is normally within 8 - 24 hours.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
Viscosity 750 cP
750 cP
Mechanical Properties Metric English Comments
Tensile Strength, Yield 18.6 MPa
2700 psi
Adhesive Bond Strength 29.6 MPa
4300 psi
Steel lap shear
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 93.3 °C
200 °F
Minimum Service Temperature, Air -51.1 °C
-60.0 °F
Processing Properties Metric English Comments
Cure Time >= 0.200 min
>= 0.00333 hour
480 min
8.00 hour
Full cure
Descriptive Properties Value Comments
Base Ethyl
Color Clear
Gap Fill (mil) 7