Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Renegade Materials Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Developed using state-of-the-art formulating technologies, RM-3000 One Part BMI RTM Resin delivers superior hot/wet performance in airframe, missile and propulsion applications at service temperatures up to 400°F. RM-3000 resin delivers improved damage tolerance at higher temperatures vs. industry-standard BMI resins. RM-3000 resin can be injected into a variety of woven and non-crimp fabrics as well as braids and complex engineered preforms. Renegade also offers a similar resin system for Vacuum Assisted RTM (VARTM) processing to support molding of larger parts called RM-3010 and an autoclave prepreg version called RM-3002.Information provided by Renegade Materials Corporation.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
Resin
Mechanical Properties Metric English Comments
Elongation at Break 4.0 %
4.0 %
Resin, RT, Dry
1.4 %

@Temperature 177 °C
1.4 %

@Temperature 350 °F
Wet (140°F/95% RH), 0° Direction; ASTM D6641
2.3 %

@Temperature 21.1 °C
2.3 %

@Temperature 70.0 °F
Dry, 0° Direction; ASTM D6641
Flexural Strength 145 MPa
21000 psi
Resin
Flexural Modulus 4.27 GPa
620 ksi
Resin
Compressive Strength 352 MPa

@Temperature 177 °C
51000 psi

@Temperature 350 °F
Wet (140°F/95% RH), 0° Direction; ASTM D6641
710 MPa

@Temperature 21.1 °C
103000 psi

@Temperature 70.0 °F
Dry, 0° Direction; ASTM D6641
Compressive Modulus 28.3 GPa

@Temperature 177 °C
4100 ksi

@Temperature 350 °F
Wet (140°F/95% RH), 0° Direction
33.8 GPa

@Temperature 21.1 °C
4900 ksi

@Temperature 70.0 °F
Dry, 0° Direction; ASTM D6641
Shear Strength 33.1 MPa

@Temperature 177 °C
4800 psi

@Temperature 350 °F
Wet (140°F/95% RH), In-plane; ASTM D3846
96.5 MPa

@Temperature 21.1 °C
14000 psi

@Temperature 70.0 °F
Dry, In-plane; ASTM D3846
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 247 °C
477 °F
Wet, Resin, Storage Modulus
282 °C
540 °F
Dry, Resin, Storage Modulus