Constellium PLAN 6082 Aluminum Rolled Plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name PLAN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium PLAN 6082 Aluminum Rolled Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensive machining. Typical applications include parts for printing and packaging machines, as well as conveying systemsInformation provided by manufacturer
Physical Properties Metric English Comments
Density 2.70 g/cc
0.0975 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 105

@Thickness 4.00 - 8.00 mm
 105

@Thickness 0.157 - 0.315 in
105

@Thickness 8.00 - 25.0 mm
 105

@Thickness 0.315 - 0.984 in
105

@Thickness 25.0 - 60.0 mm
 105

@Thickness 0.984 - 2.36 in
105

@Thickness 60.0 - 150 mm
 105

@Thickness 2.36 - 5.91 in
Tensile Strength >= 275 MPa

@Thickness 100 - 150 mm
 >= 39900 psi

@Thickness 3.94 - 5.91 in
 Temper T651; Standard EN 485-2
>= 295 MPa

@Thickness 12.5 - 60.0 mm
 >= 42800 psi

@Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 295 MPa

@Thickness 60.0 - 100 mm
 >= 42800 psi

@Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 300 MPa

@Thickness 6.00 - 12.5 mm
 >= 43500 psi

@Thickness 0.236 - 0.492 in
 Temper T651; Standard EN 485-2
>= 310 MPa

@Thickness 4.00 - 6.00 mm
 >= 45000 psi

@Thickness 0.157 - 0.236 in
 Temper T651; Standard EN 485-2
335 MPa

@Thickness 4.00 - 8.00 mm
 48600 psi

@Thickness 0.157 - 0.315 in
 Typical Strength; Standard EN 485-2
350 MPa

@Thickness 8.00 - 25.0 mm
 50800 psi

@Thickness 0.315 - 0.984 in
 Typical Strength; Standard EN 485-2
350 MPa

@Thickness 25.0 - 60.0 mm
 50800 psi

@Thickness 0.984 - 2.36 in
 Typical Strength; Standard EN 485-2
350 MPa

@Thickness 60.0 - 150 mm
 50800 psi

@Thickness 2.36 - 5.91 in
 Typical Strength; Standard EN 485-2
Tensile Strength, Yield >= 240 MPa

@Strain 0.200 %,
Thickness 12.5 - 60.0 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 240 MPa

@Strain 0.200 %,
Thickness 60.0 - 100 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 240 MPa

@Strain 0.200 %,
Thickness 100 - 150 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 3.94 - 5.91 in
 Temper T651; Standard EN 485-2
>= 255 MPa

@Strain 0.200 %,
Thickness 6.00 - 12.5 mm
 >= 37000 psi

@Strain 0.200 %,
Thickness 0.236 - 0.492 in
 Temper T651; Standard EN 485-2
>= 260 MPa

@Strain 0.200 %,
Thickness 4.00 - 6.00 mm
 >= 37700 psi

@Strain 0.200 %,
Thickness 0.157 - 0.236 in
 Temper T651; Standard EN 485-2
300 MPa

@Strain 0.200 %,
Thickness 4.00 - 8.00 mm
 43500 psi

@Strain 0.200 %,
Thickness 0.157 - 0.315 in
 Typical Strength; Standard EN 485-2
305 MPa

@Strain 0.200 %,
Thickness 8.00 - 25.0 mm
 44200 psi

@Strain 0.200 %,
Thickness 0.315 - 0.984 in
 Typical Strength; Standard EN 485-2
310 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 45000 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Typical Strength; Standard EN 485-2
310 MPa

@Strain 0.200 %,
Thickness 60.0 - 150 mm
 45000 psi

@Strain 0.200 %,
Thickness 2.36 - 5.91 in
 Typical Strength; Standard EN 485-2
Elongation at Break >= 6.0 %

@Thickness 100 - 150 mm
 >= 6.0 %

@Thickness 3.94 - 5.91 in
 Temper T651; Standard EN 485-2
>= 7.0 %

@Thickness 60.0 - 100 mm
 >= 7.0 %

@Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 8.0 %

@Thickness 12.5 - 60.0 mm
 >= 8.0 %

@Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 9.0 %

@Thickness 6.00 - 12.5 mm
 >= 9.0 %

@Thickness 0.236 - 0.492 in
 Temper T651; Standard EN 485-2
>= 10 %

@Thickness 4.00 - 6.00 mm
 >= 10 %

@Thickness 0.157 - 0.236 in
 Temper T651; Standard EN 485-2
11 %

@Thickness 8.00 - 25.0 mm
 11 %

@Thickness 0.315 - 0.984 in
 Typical Elongation; Standard EN 485-2
11 %

@Thickness 25.0 - 60.0 mm
 11 %

@Thickness 0.984 - 2.36 in
 Typical Elongation; Standard EN 485-2
11 %

@Thickness 60.0 - 150 mm
 11 %

@Thickness 2.36 - 5.91 in
 Typical Elongation; Standard EN 485-2
14 %

@Thickness 4.00 - 8.00 mm
 14 %

@Thickness 0.157 - 0.315 in
 Typical Elongation; Standard EN 485-2
Modulus of Elasticity 69.0 GPa
10000 ksi
Thermal Properties Metric English Comments
CTE, linear 23.4 µm/m-°C

@Temperature 20.0 - 100 °C
 13.0 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 150 - 170 W/m-K
1040 - 1180 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 95.3 - 98.3 %
95.3 - 98.3 %
as balance
Chromium, Cr <= 0.25 %
<= 0.25 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 0.60 - 1.2 %
0.60 - 1.2 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si 0.70 - 1.3 %
0.70 - 1.3 %
Zinc, Zn <= 0.20 %
<= 0.20 %
Zr+Ti <= 0.15 %
<= 0.15 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000360 - 0.00000420 ohm-cm
0.00000360 - 0.00000420 ohm-cm
Temper T651