Polymer Property : Shear Strength = 33.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	33.1 MPa @Temperature 177 °C	4800 psi @Temperature 350 °F	Short-Beam, Dry; ASTM D2344
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Shear Strength	33.1 MPa @Temperature 177 °C	4800 psi @Temperature 350 °F	Wet (140°F/95% RH), In-plane; ASTM D3846
Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric Developed using state-of-the-art formulating technologies, RM-3000 One Part BMI RTM Resin delivers superior hot/wet performance in airframe, missile and propulsion applications at service temperatu..
Shear Strength	33.1 MPa @Temperature 175 °C	4800 psi @Temperature 347 °F	Laminate property; In Line Shear; Conditioning: 14 days Water 158°F
Hexcel® HexFlow® RTM651 One-part Modified BMI Resin HexFlow® RTM651 is a one-component modified bismaleimide for resin transfer molding (RTM). Upon heating to 212-248°F, the resin will become a low viscosity homogeneous liquid that has a long pot-l..
Shear Strength	33.1 MPa @Temperature 71.1 °C	4800 psi @Temperature 160 °F	Lap Shear
Hexcel® Redux® 312 Modified epoxy film adhesive (0.015 psf) Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support..
Shear Strength	33.1 MPa @Temperature 21.1 °C	4800 psi @Temperature 70.0 °F	Lap Shear
Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 ..