Precision Polymer Engineering Perlast® G92A Perfluoroelastomer

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Precision Polymer Engineering Limited
Trade Name	Perlast®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Precision Polymer Engineering Perlast® G92A Perfluoroelastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

An electrically conductive black perfluoroelastomer with excellent chemical and steam resistance.Applications: Specially formulated for applications requiring special electrical properties. Originally designed for “Microfluidics” and “Lab on a Chip” applications, this material possesses good resistance to reagents and solvents whilst providing protection against static electricity build up. It has no capacitance, and a volume resistivity circa 200 ohm/cm. Do not use any Perlast ® grade with molten alkali metals.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	94	94	°IRHD; ASTM D1415
	95	95	°IRHD, +1 change after 72 hours @ 250°C; ASTM D1415
Tensile Strength, Yield	16.15 MPa	2342 psi	-15% change after 72 hours @ 250°C; ASTM D412
	19.0 MPa	2760 psi	ASTM D412
Elongation at Break	68 %	68 %	ASTM D412
	88.4 %	88.4 %	30% change after 72 hours @ 250°C; ASTM D412
50% Modulus	0.0129 GPa	1.87 ksi	15% change after 72 hours @ 250°C; ASTM D412
Compression Set	36 %	36 %	24 hours @ 200°C; ASTM D395

Thermal Properties	Metric	English
Maximum Service Temperature, Air	260 °C	500 °F
Minimum Service Temperature, Air	-15.0 °C	5.00 °F
Flash Point	>= 400 °C	>= 752 °F