PolyOne Geon™ Vinyl Wire & Cable EMB405LU Polyvinyl Chloride, Flexible (PVC, Flexible)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Wire & Cable EMB405LU Polyvinyl Chloride, Flexible (PVC, Flexible).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 89
89
15 sec; ASTM D2240
Tensile Strength, Yield 20.7 MPa
3000 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 300 %
300 %
Type IV, 510 mm/min; ASTM D638
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
UL Temperature Rating
Brittleness Temperature -20.0 °C
-4.00 °F
ASTM D746
Oxygen Index 30 %

@Thickness 3.18 mm
30 %

@Thickness 0.125 in
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 5.60e+15 ohm-cm
5.60e+15 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 177 - 188 °C
351 - 370 °F
Descriptive Properties Value Comments
Agency Ratings UL QMTT2
UL VW-1
Features Flame Retardant
Sunlight Resistant (720 hours)
Forms Pellets
Generic Material PVC, Flexible
Generic Name Polyvinyl Chloride, Flexible (PVC, Flexible)
Processing Method Extrusion Coating
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Retention of Tensile Elongation 91%
136°C, 762.0 µm; 168 hr, UL Standard
Retention of Tensile Strength 100%
136°C, 762.0 µm; 168 hr, UL Standard
RoHS Compliance RoHS Compliant
Uses Building Wire Insulation
Wire & Cable Applications
Wire Types THHN
THW
THWN
TW