Network Polymers NPP 25-0202 C
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers NPP 25-0202 C.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Copolymer Polypropylene, Clarified RandomInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
| Elongation at Yield | 11 % | 11 % | ASTM D638 |
| Flexural Modulus | 0.931 GPa | 135 ksi | Test Method I, Procedure B (chs speed 0.05 in/min), 1 % Secant; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm @Temperature -18.0 °C |
4.00 ft-lb/in @Temperature -0.400 °F |
ASTM D256 |
| Gardner Impact | 22.60 J | 16.67 ft-lb | STP 2223 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MR 50 U Linear Low Density Polyethylene
- Techmer ES Elastoblend® PA6/66 IM3 BK
- Teknor Apex TEKRON® 4200-70 Thermoplastic Elastomer
- A. Schulman POLYFLAM™ RPP 1221 Low-Blooming, General Purpose Copolymer Polypropylene
- Tisan TISARBON® 10% Glass Fiber Reinforced Polycarbonate
- Compuestos Dominicanos Polycom C-550170 PVC
- 3M Scotchcal™ 8000-15 Graphic Film
- Haynes 25 alloy, room temperature after 20% cold reduction
Copyright © lookpolymers.com All Rights Reserved