NOVA Chemicals Sclair® 11N1 PE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11N1 PE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low gel, Excellent seal characteristics, Easy processabilityApplications: Premium shrink film, Co-extrusionFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 25.0 - 75.0 microns | 0.984 - 2.95 mil | |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Break, TD | 920 % | 920 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | at 1%; ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | F<sub>50</sub>, ASTM D1709/A |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | 1 mil; ASTM D1003 |
| Gloss | 51 % | 51 % | at 45°; 1 mil; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |
| Die Opening | 0.0900 - 0.220 cm | 0.0354 - 0.0866 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blow Up Ratio | 2:1 to 3:1 |