Multibase C6-250 VAROX DBPH Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-250 VAROX DBPH Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 56
56
molded- without post cure; ASTM D2240
58
58
post cured- 2 hours at 177°C; ASTM D2240
58
58
post cured- 4 hours at 177°C; ASTM D2240
60
60
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 7.58 MPa
1100 psi
molded-without post cure; ASTM D412
8.96 MPa
1300 psi
post cured- 2 hours at 177°C; ASTM D412
8.96 MPa
1300 psi
post cured- 4 hours at 177°C; ASTM D412
8.96 MPa
1300 psi
post cured- 8 hours at 177°C; ASTM D412
Tensile Strength, Yield 2.96 MPa
430 psi
at 200%, molded-without post cure; ASTM D412
3.31 MPa
480 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
3.38 MPa
490 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.86 MPa
560 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 460 %
460 %
post cured- 8 hours at 177°C; ASTM D412
520 %
520 %
post cured- 4 hours at 177°C; ASTM D412
520 %
520 %
molded-without post cure; ASTM D412
530 %
530 %
post cured- 2 hours at 177°C; ASTM D412
Tear Strength 28.0 kN/m
160 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
35.1 kN/m
200 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
36.8 kN/m
210 pli
Die B,molded-without post cure; ASTM D624
36.8 kN/m
210 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
Compression Set 46 %
46 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
48 %
48 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
57 %
57 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
67 %
67 %
22 hours at 177°C, molded-without post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 3.00 %

@Temperature 177 °C,
Time 7200 sec
3.00 %

@Temperature 351 °F,
Time 2.00 hour
post cured
3.00 %

@Temperature 177 °C,
Time 14400 sec
3.00 %

@Temperature 351 °F,
Time 4.00 hour
post cured
3.30 %

@Temperature 177 °C,
Time 28800 sec
3.30 %

@Temperature 351 °F,
Time 8.00 hour
post cured