Lotte Chemical Titan TITANEX® LF1051 Linear low density polyethylene Hexene-1 resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lotte Chemical Titan TITANEX® LF1051 Linear low density polyethylene Hexene-1 resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LF1051 is a pelleted linear low density polyethylene Hexene-1 resin formulated with antioxidant, high antiblock and slip agent. This product is used for blown film extrusion which offers outstanding toughness, extrudability and draw down ability.Applications: High strength film, trash bags.Advantages: Outstanding puncture strength, impact strength and tear strength.Information provided by Titan Chemicals
Physical Properties Metric English Comments
Base Resin Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
extruded at 2:1 BUR
Base Resin Melt Index 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Elmendorf Tear Strength, MD 18.0 g/micron
457 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 29.0 g/micron
737 g/mil
ASTM D1922
Dart Drop 8.00 g/micron
203 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 49.0 MPa
7110 psi
ASTM D882
Film Tensile Strength at Break, TD 36.3 MPa
5260 psi
ASTM D882
1% Secant Modulus, MD 196.14 MPa
28447 psi
ASTM D882
1% Secant Modulus, TD 225.56 MPa
32714 psi
ASTM D882
Optical Properties Metric English Comments
Haze 15 %
15 %
ASTM D1003
Gloss 50 %
50 %
45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 180 - 200 °C
356 - 392 °F
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0