LG Chemical TR552 MABS, Transparency, High Impact, Chemical Resistance

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical TR552 MABS, Transparency, High Impact, Chemical Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Transparency, High Impact, Chemical ResistanceApplication: Electric/Electronic Applications, Copier, Printer etcCAS No. 9011-14–7 and 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Melt Flow 12 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 12 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength, Yield 39.2 MPa

@Thickness 3.20 mm
 5690 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 35 %

@Thickness 3.20 mm
 35 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 60.8 MPa

@Thickness 6.40 mm
 8820 psi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 1.83 GPa

@Thickness 6.40 mm
 266 ksi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.26 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 4.22 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
2.26 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.22 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 6.40 mm
 180 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Optical Properties Metric English Comments
Haze 2.2 %
2.2 %
ASTM D1003
Transmission, Visible 90 %
90 %
ASTM D1003