- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Ineos ABS Lustran® 130
Ineos ABS Lustran® 130
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 130.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingSheet extrusionBlow moldingThermoforming
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.1 MPa | 5090 psi | |
| Elongation at Break | 29 % | 29 % | Nominal |
| Elongation at Yield | 3.3 % | 3.3 % | |
| Tensile Modulus | 2.14 GPa | 310 ksi | |
| Charpy Impact, Notched | 3.80 J/cm² | 18.1 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 94.0 µm/m-°C @Temperature 20.0 °C |
52.2 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 55.0 MPa | 7980 psi |