- Hexcel® HexPly® F185 Epoxy Resin, 1581 Glass Fabric
Hexcel® HexPly® F185 Epoxy Resin, 1581 Glass Fabric
| Category | Polymer , Thermoset , Epoxy , Epoxy/Glass SMC |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F185 Epoxy Resin, 1581 Glass Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: 1581-38"-F185; Fiber: 150-1/2Information provided by HexCel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | 0.40 - 1.2 % | 0.40 - 1.2 % | Prepreg |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 2.779 MPa @Temperature 82.0 °C |
403.1 psi @Temperature 180 °F |
Flatwise TS |
| 5.537 MPa @Temperature 24.0 °C |
803.1 psi @Temperature 75.2 °F |
Flatwise TS | |
| 8.432 MPa @Temperature -54.0 °C |
1223 psi @Temperature -65.2 °F |
Flatwise TS | |
| 379 MPa @Temperature 24.0 °C |
55000 psi @Temperature 75.2 °F |
Warp TS | |
| Compressive Yield Strength | 345 MPa @Temperature 24.0 °C |
50000 psi @Temperature 75.2 °F |
Warp compression |
| Shear Strength | 28.427 MPa @Temperature 82.0 °C |
4123.0 psi @Temperature 180 °F |
Lap shear |
| 31.778 MPa @Temperature 24.0 °C |
4609.0 psi @Temperature 75.2 °F |
Lap shear | |
| 37.08 MPa @Temperature -54.0 °C |
5378 psi @Temperature -65.2 °F |
Lap shear | |
| Peel Strength | 8.24 kN/m @Temperature -54.0 °C |
47.0 pli @Temperature -65.2 °F |
Metal-to-metal |
| 11.1 kN/m @Temperature 82.0 °C |
63.3 pli @Temperature 180 °F |
Metal-to-metal | |
| 12.8 kN/m @Temperature 24.0 °C |
73.0 pli @Temperature 75.2 °F |
Metal-to-metal |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.023 | Laminate |
| Fiber Volume (%) | 51.3 | Laminate |
| Flow (%) | 24-34 | |
| Wet Resin Content (%) | 47-53 | Prepreg |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 N-S20 Nylon 6.6 for injection molding
- Permabond TA4310 Toughened Acrylic Adhesive
- Gwent Electronic Materials P2121112P6 Oxygen Plasma Modified Graphene Nanoplatelets
- Techmer ES HiFill FR® PA6 GF33 FR HS L 33% Glass Filled (Dry)
- A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene
- DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
- ExxonMobil Hicor® 30 HF 104 OHD Film
- EMS-Grivory Grivory® TSG-15/4 PA666-GF15
- BASF Ultramid® A3EG10 50% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved