Greene Tweed CHEMRAZ® 517 Perfluoroelastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Greene Tweed |
| Trade Name | CHEMRAZ® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed CHEMRAZ® 517 Perfluoroelastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Greene Tweed’s Chemraz® 517, a perfluoroelastomer, is a white specialty compound, perfect for applications where contamination from carbon black must be prevented. Chemraz 517 has a Shore A hardness value of 80. Because of its wide temperature range, -22°F to 428°F (-30°C to 220°C) Chemraz 517 is well suited for use in a range of applications, from mechanical seals to mixersAvailable for use as O-rings, gaskets and many other custom shapesApplications:Mechanical sealsSampling/metering equipmentPump housingsInformation provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.22 g/cc | 2.22 g/cc | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D1414 |
| Tensile Strength, Yield | 3.72 MPa | 540 psi | @ 50% Elongation; ASTM D1414 |
| 7.24 MPa | 1050 psi | @100% Elongation; ASTM D1414 | |
| Elongation at Break | 165 % | 165 % | ASTM D1414 |
| Compression Set | 25 % | 25 % | 70 hours @ 400°F (204°C) @ 25% deflection; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |