Fujipoly Industries Sarcon® 85Q Thin-Film QR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 85Q Thin-Film QR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon QR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 54
54
60°C for 500 hrs with 95% RH; ASTM D2240
55
55
ASTM D2240
66
66
150°C for 1,000 hrs; ASTM D2240
78
78
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 2.352 MPa
341.1 psi
2.941 MPa
426.6 psi
60°C for 500 hrs with 95% RH
4.705 MPa
682.4 psi
150°C for 1,000 hrs
5.647 MPa
819.0 psi
200°C for 1,000 hrs
Elongation at Yield 77 %
77 %
200°C for 1,000 hrs
113 %
113 %
173 %
173 %
60°C for 500 hrs with 95% RH
250 %
250 %
Tear Strength 1.10 kN/m
6.28 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 3.50e+14 ohm-cm
3.50e+14 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
4.10e+15 ohm-cm
4.10e+15 ohm-cm
150°C for 1,000 hrs
8.00e+15 ohm-cm
8.00e+15 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 4.82

@Frequency 1e+6 Hz
 4.82

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
4.83

@Frequency 1000 Hz
 4.83

@Frequency 1000 Hz
 After 1000 hrs at 150°C
4.85

@Frequency 1e+6 Hz
 4.85

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
4.86

@Frequency 50 Hz
 4.86

@Frequency 50 Hz
 After 1000 hrs at 150°C
4.88

@Frequency 1000 Hz
 4.88

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
4.88

@Frequency 1e+6 Hz
 4.88

@Frequency 1e+6 Hz
4.89

@Frequency 1e+6 Hz
 4.89

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
4.9

@Frequency 1000 Hz
 4.9

@Frequency 1000 Hz
4.92

@Frequency 1000 Hz
 4.92

@Frequency 1000 Hz
 After 1000 hrs at 200°C
4.94

@Frequency 50 Hz
 4.94

@Frequency 50 Hz
4.94

@Frequency 50 Hz
 4.94

@Frequency 50 Hz
 After 1000 hrs at 200°C
4.94

@Frequency 50 Hz
 4.94

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Dielectric Strength 11.0 kV/mm
279 kV/in
AC 60 Hz
16.0 kV/mm
406 kV/in
150°C for 1,000 hrs
17.0 kV/mm
432 kV/in
60°C for 500 hrs with 95% RH
18.0 kV/mm
457 kV/in
200°C for 1,000 hrs
Dielectric Breakdown 11000 V
11000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0016

@Frequency 1e+6 Hz
 0.0016

@Frequency 1e+6 Hz
0.0018

@Frequency 1e+6 Hz
 0.0018

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.0018

@Frequency 1e+6 Hz
 0.0018

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0024

@Frequency 50 Hz
 0.0024

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0024

@Frequency 1000 Hz
 0.0024

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0025

@Frequency 1e+6 Hz
 0.0025

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0027

@Frequency 1000 Hz
 0.0027

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0029

@Frequency 50 Hz
 0.0029

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0032

@Frequency 1000 Hz
 0.0032

@Frequency 1000 Hz
0.0053

@Frequency 1000 Hz
 0.0053

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.0069

@Frequency 50 Hz
 0.0069

@Frequency 50 Hz
0.0103

@Frequency 50 Hz
 0.0103

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color Grey
Thermal Impedance 1.25°C/W
FTM P-3010; ASTM D5470