ExxonMobil Oppalyte™ 30MD447 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Oppalyte™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Oppalyte™ 30MD447 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for use on VFFS and HFFS machines and is also very well suited for overwrapping applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent stiffness and flex resistance Good seal strengthExcellent dimensional stabilityGood hot slipGood hot tackFeatures:In Lamination Lap SealableLight BarrierApplications:BakeryBiscuits/Cookie/CrackersBox OverwrapConfectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold DetergentsIce CreamPet Food Uses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPouches-Flexible PackagingVFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.10 g/m²/day @Temperature 23.0 °C	0.0710 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.97 g/m²/day @Temperature 38.0 °C	0.320 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Thickness	30.5 microns	1.20 mil	ExxonMobil Method
Coating Weight	23.5 g/m²	14.7 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	160 %	160 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	65 %	65 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	1.70 GPa	247 ksi	MD; ExxonMobil Method
	3.20 GPa	464 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Untreated Surface; ExxonMobil Method
	0.30	0.30	Treated Surface; ExxonMobil Method
Seal Strength	410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	410 g/in @Pressure 40.0 psi, Temperature 284 °F	Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	120 MPa	17400 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	200 MPa	29000 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	3.0 % @Temperature 135 °C, Time 432 sec	3.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	3.0 % @Temperature 135 °C, Time 432 sec	3.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Gloss	55 %	55 %	45°; ExxonMobil Method
Transmission, Visible	33 %	33 %	ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	45°F	Untreated, 36.3 psi, 0.2 sec
	72°F	Treated, 36.3 psi, 0.2 sec
Whiteness Index	90
Yield	29200 in²/lb