Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Film Tensile Strength at Break, MD = 120 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 120 MPa

@Thickness 0.125 mm
17400 psi

@Thickness 0.00492 in
ISO 527
Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline
APTIV PEEK 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTI..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ISO 527
Victrex® APTIV® 1300-050G Polyetheretherketone (PEEK) Polymer Film
DescriptionAPTIV® 1300 film is the black version of unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance ..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ISO 527
Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous
APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK ..
Film Tensile Strength at Break, MD 120 MPa

@Thickness 0.0250 mm
17400 psi

@Thickness 0.000984 in
ISO 527
Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous
APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK ..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML11 General Grade BOPP Matt Film (thickness: 15 µm)
ML11 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. One side has corona treatment. It is specially designed for board laminati..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML11 General Grade BOPP Matt Film (thickness: 18 µm)
ML11 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. One side has corona treatment. It is specially designed for board laminati..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML11 General Grade BOPP Matt Film (thickness: 20 µm)
ML11 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. One side has corona treatment. It is specially designed for board laminati..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML11 General Grade BOPP Matt Film (thickness: 30 µm)
ML11 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. One side has corona treatment. It is specially designed for board laminati..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML21 General Grade BOPP Matt Film (thickness: 15 µm)
ML21 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. Both sides have corona treatment. It is specially designed for board lamin..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML21 General Grade BOPP Matt Film (thickness: 18 µm)
ML21 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. Both sides have corona treatment. It is specially designed for board lamin..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML21 General Grade BOPP Matt Film (thickness: 20 µm)
ML21 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. Both sides have corona treatment. It is specially designed for board lamin..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ASTM-D882
Kinlead ML21 General Grade BOPP Matt Film (thickness: 30 µm)
ML21 is a general grade BOPP Matt film. It is translucent and non heat sealable. It has low static and a good matt surface. Both sides have corona treatment. It is specially designed for board lamin..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 35MB666 OPP Film
Product Description: A is a biaxially oriented transparent polypropylene film, acrylic coated tow sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle E..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 40MB666 OPP Film
Product Description: A is a biaxially oriented transparent polypropylene film acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle Ea..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 40MB668 OPP Film
Product Description: A high speed transparent biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provides excellent perfo..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 42MB777 OPP Film
Product Description: A high gas barrier, biaxially oriented transparent PP film, coated one side PVdC, one side acrylic, This film provides outstanding performance on all packaging machines.Availabi..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 52MBR666 OPP Film
Product Description: Bicor 52MBR666 is a biaxially oriented transparent polypropylene film coated with humidity resistant acrylic on both sides. This film is designed to wrap products with a high mo..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 35LL666 OPP Film
Product Description: A transparent, high gloss, two side acrylic coated BOPP film for reel-fed wrap-around labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Featur..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 40LL666 OPP Film
Product Description: A transparent, high gloss, two side acrylic coated BOPP film for reel-fed wrap-around labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Featur..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 50LGT702 OPP Film
Product Description: A transparent biaxially oriented polypropylene film coated one side resistant coating and one side with a specially formulated acrylic coating. This film is designed for cut and..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 50LL210 OPP Film
Product Description: An uncoated biaxially oriented, transparent polypropylene film for Pressure Sensitive labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Featur..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 50LL539 OPP Film
Product Description: A clear, two-side coated, polypropylene label face stock designed for demanding pressure sensitive applications where outstanding ink adhesion and adhesive anchorage are require..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 50LL539 OPP Film
Product Description: A clear, two-side treated, polypropylene label facestock designed for demanding pressure sensitive applications where outstanding ink adhesion and adhesive anchorage are require..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 50ML580 OPP Film
Product Description: A metalized, surface printable OPP film designed for pressure sensitive applications where high-sheen metalized appearance and high-speed press performance are desired. The prop..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 35MD447 OPP Film
Product Description: A coextruded super white opaque, modified high density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for use..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 57LL210 OPP Film
Product Description: An uncoated biaxially oriented, transparent polypropylene film for Pressure Sensitive labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Featur..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 30MD447 OPP Film
Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 40MD447 OPP Film
Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u..
Film Tensile Strength at Break, MD 120 MPa
17400 psi
ISO 527
Victrex® APTIV® 1300-100G Polyetheretherketone (PEEK) Polymer Film
DescriptionAPTIV® 1300 film is the black version of unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance ..