ExxonMobil LLDPE LL 3402.48 Cast Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LLDPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LLDPE LL 3402.48 Cast Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LL 3402.48 is a hexane medium density polyethylene cast film grade for applications requiring high stiffness. It can also be used in blown films. Films produced from this resin exhibit good tensile and puncture resistance properties.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: No Thermal Stabilizer: YesApplications: Agricultural FilmCast FilmDiaper BacksheetOverwrap FilmInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ExxonMobil method |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 15.2 MPa | 2200 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 15.9 MPa | 2300 psi | ASTM D882 |
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 |
| Film Elongation at Break, TD | 880 % | 880 % | ASTM D882 |
| Puncture Energy | 1.05 J | 0.775 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 360 g | 360 g | ASTM D1922 |
| Dart Drop Test | <= 50.0 g | <= 0.110 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 68.9 MPa | 10000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 39.3 MPa | 5700 psi | ASTM D882 |
| 1% Secant Modulus, MD | 379 MPa | 55000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 427 MPa | 62000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 262 °C | <= 504 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.9 % | 2.9 % | ASTM D1003 |
| Gloss | 87 % | 87 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 7 lbf | ExxonMobil Method |