ExxonMobil LL 8555.67 Rotational Molding Resin  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 8555.67 Rotational Molding Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL 8555 is a linear low density hexene copolymer designed to offer excellent processability, dimensional control, whiteness and low warpage. This resin is ideally suited for applications that require excellent surface appearance and the optimum balance of ESCR, stiffness, and toughness properties.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ASTM D4883
ESCR 100% Igepal® 275 hour
275 hour
ASTM D1693
ESCR 10% Igepal® 55 hour
55 hour
ASTM D1693
Melt Flow 6.8 g/10 min
6.8 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.2 MPa
2500 psi
ASTM D638
Elongation at Yield 17.5 %
17.5 %
ASTM D638
Flexural Modulus 0.703 GPa
102 ksi
1% secant; ASTM D790
Impact Test 81.3 J

@Thickness 3.17 mm,
Temperature -40.0 °C
60.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM
217 J

@Thickness 6.35 mm,
Temperature -40.0 °C
160 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM
Thermal Properties Metric English Comments
Melting Point 126 °C
259 °F
ASTM D3418
Crystallization Temperature 112.1 °C
233.8 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 59.0 °C
138 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 38.0 °C
100 °F
ASTM D648
Descriptive Properties Value Comments
Features Standard processing antioxidants
Form PELLET