ExxonMobil LD 302.56 High Clarity, High Impact Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 302.56 High Clarity, High Impact Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 302 Series films exhibit superior impact strength, good heat sealability, and good low temperature properties. Typical applications are frozen food packaging or other food packaging.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil Method
Vinyl Acetate Content 3.5 %
3.5 %
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.3 g/10 min
1.3 g/10 min
ExxonMobil Method
Antiblock Level 3000 ppm
3000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.27 MPa
1200 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 8.14 MPa
1180 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 190 %
190 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Film Elongation at Yield, MD 6.7 %
6.7 %
ASTM D882
Film Elongation at Yield, TD 5.7 %
5.7 %
ASTM D882
Elmendorf Tear Strength MD 190 g
190 g
ASTM D1922
Elmendorf Tear Strength TD 110 g
110 g
ASTM D1922
Elmendorf Tear Strength, MD 4.984 g/micron
126.6 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.89 g/micron
73.3 g/mil
ASTM D1922
Dart Drop 4.461 g/micron
113.3 g/mil
ASTM D1709
Dart Drop Test 170 g
0.375 lb
ASTM D1709
Film Tensile Strength at Break, MD 24.2 MPa
3510 psi
ASTM D882
Film Tensile Strength at Break, TD 23.2 MPa
3370 psi
ASTM D882
1% Secant Modulus, MD 146 MPa
21200 psi
ASTM D882
1% Secant Modulus, TD 172 MPa
24900 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 105 °C
221 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 92.0 °C
198 °F
ExxonMobil Method
Vicat Softening Point 88.3 °C
191 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 69 %
69 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Descriptive Properties Value Comments
Features Thermal Stabilizer