ExxonMobil LD 105.30 Very High Clarity Packaging Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 105.30 Very High Clarity Packaging Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 105 resins are homopolymer packaging film resins designed for applications requiring outstanding clarity with good stiffness. These resins can be processed in either blown or cast film equipment. In blown film equipment LD 105.30 can be drawn down to 1.0 mil gauge.Availability: Latin America, North America and South America Additive: Antiblock: 1000 ppmSlip: NoThermal Stabilizer: YesApplications: Blend PartnerBread BagsDisplay Packaging FilmFood packagingForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmHigh Quality LaminationLamination FilmLaundry FilmLight Duty Shrink FilmProduce BagsSalad BagsTextile Packaging Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1000 ppm
1000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 210 %
210 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Puncture Energy 0.757 J
0.558 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 350 g
350 g
ASTM D1922
Elmendorf Tear Strength TD 180 g
180 g
ASTM D1922
Dart Drop Test 100 g
0.221 lb
ASTM D1709
Film Tensile Strength at Break, MD 24.9 MPa
3610 psi
ASTM D882
Film Tensile Strength at Break, TD 21.4 MPa
3100 psi
ASTM D882
1% Secant Modulus, MD 214 MPa
31000 psi
ASTM D882
1% Secant Modulus, TD 255 MPa
37000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 111 °C
232 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 5.2 %
5.2 %
ASTM D1003
Gloss 76 %
76 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Descriptive Properties Value Comments
Features Thermal Stabilizer