ExxonMobil EXACT™ 3024 Plastomer for Cast Film Applications

Category	Polymer , Film , Thermoplastic , Elastomer, TPE
Manufacturer	Exxon Chemical
Trade Name	EXACT™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil EXACT™ 3024 Plastomer for Cast Film Applications.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Exact 3024 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. It can be used for both monolayer and multilayer coextruded cast film applications requiring excellent heat sealing performance. Typical applications include food packaging seal layers and lamination films. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications:Cast Film Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ExxonMobil Method
Thickness	25.4 microns	1.00 mil
Melt Flow	4.5 g/10 min	4.5 g/10 min	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	5.72 MPa	830 psi	2% Offset; ASTM D882
Film Tensile Strength at Yield, TD	4.96 MPa	720 psi	2% Offset; ASTM D882
Film Elongation at Break, MD	560 %	560 %	ASTM D882
Film Elongation at Break, TD	780 %	780 %	ASTM D882
Film Elongation at Yield, MD	9.0 %	9.0 %	ASTM D882
Film Elongation at Yield, TD	7.2 %	7.2 %	ASTM D882
Puncture Energy	4.58 J	3.37 ft-lb	ExxonMobil Method
Elmendorf Tear Strength, MD	1.97 g/micron	50.0 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	5.91 g/micron	150 g/mil	ASTM D1922
Dart Drop	5.51 g/micron	140 g/mil	ASTM D1709A
Film Tensile Strength at Break, MD	47.5 MPa	6890 psi	ASTM D882
Film Tensile Strength at Break, TD	31.6 MPa	4590 psi	ASTM D882
1% Secant Modulus, MD	85.5 MPa	12400 psi	ASTM D882
1% Secant Modulus, TD	97.2 MPa	14100 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	97.2 °C	207 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	82.0 °C	180 °F	ExxonMobil Method
Vicat Softening Point	87.2 °C	189 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	0.80 %	0.80 %	ASTM D1003
Gloss	93 %	93 %	ASTM D2457