Eastman Tenite 264-16 CAB Cellulose Acetate Butyrate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 264-16 CAB Cellulose Acetate Butyrate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
16% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 23.0 MPa
3340 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Elongation at Yield 3.6 %
3.6 %
Tensile Modulus 1.01 GPa
146 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 2.12 J/cm²
10.1 ft-lb/in²
0.740 J/cm²

@Temperature -30.0 °C
 3.52 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 129 µm/m-°C

@Temperature 20.0 °C
 71.7 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 168 µm/m-°C

@Temperature 20.0 °C
 93.3 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Vicat Softening Point 80.0 °C
176 °F
Glass Transition Temp, Tg 98.0 °C
208 °F
Processing Properties Metric English Comments
Melt Temperature 205 - 215 °C
401 - 419 °F