California Fine Wire Copper, 27% Nickel Clad

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer California Fine Wire
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF California Fine Wire Copper, 27% Nickel Clad.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Physical Properties Metric English Comments
Density 8.89 g/cc
0.321 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 379 MPa
55000 psi
Annealed
483 MPa
70000 psi
Stress relieved
586 MPa
85000 psi
Hard
Thermal Properties Metric English Comments
Specific Heat Capacity 0.380 J/g-°C
0.0908 BTU/lb-°F
Melting Point 1100 °C
2012 °F
1170 - 1240 °C
2140 - 2260 °F
Solidus 1170 °C
2140 °F
Liquidus 1240 °C
2260 °F
Maximum Service Temperature, Air 593 °C
1100 °F
Operating Temperature
Component Elements Properties Metric English Comments
Copper, Cu 99.9 %
99.9 %
Core (Cladding is 99% Ni)
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000224 ohm-cm
0.00000224 ohm-cm
3% tolerance on sizes below 0.02, 5% tolerance on sizes above 0.02
Processing Properties Metric English Comments
Annealing Temperature 650 - 825 °C
1200 - 1520 °F
Hot-Working Temperature 925 - 1050 °C
1700 - 1920 °F
Descriptive Properties Value Comments
Temperature Coefficient of Resistance 0.003 ohms/ohm-°C
0-100°C