Borealis FA5224 Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis FA5224 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FA5224 is a Low Density Polyethylene for Film Extrusion. Contains Antioxidant, Anti-block and Medium Slip additives. This grade is developed to give strong film for medium duty applications. Applications: carrier-bag film, pouches, and general packaging film.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ISO 1183
Melt Flow 1.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Antiblock Level 850 ppm
850 ppm
talc; Borealis Method
Slip Level 450 ppm
450 ppm
erucamide; Borealis Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 300 %
300 %
ISO 527-3
Film Elongation at Break, TD 500 %
500 %
ISO 527-3
Tensile Modulus 0.180 GPa
26.1 ksi
MD/TD; ASTM D882-A
Puncture Energy 2.00 J
1.48 ft-lb
53 N; 40µm sample; ASTM D5748
Coefficient of Friction 0.15
0.15
Dynamic; ISO 8295
Elmendorf Tear Strength, MD 10.19 g/micron
258.8 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 5.096 g/micron
129.4 g/mil
ISO 6383/2
Dart Drop Test 140 g

@Thickness 0.0400 mm
0.309 lb

@Thickness 0.00157 in
ISO 7765-1
Film Tensile Strength at Break, MD 26.0 MPa
3770 psi
ISO 527-3
Film Tensile Strength at Break, TD 23.0 MPa
3340 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 110 °C
230 °F
ISO 11357-3
Vicat Softening Point 96.0 °C
205 °F
ISO 306
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM D1003
Gloss 85 %
85 %
ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 160 - 190 °C
320 - 374 °F