Borealis Borsoft™ SD200CF High Impact Polypropylene Random Heterophasic Copolymer for Cast Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Borealis
Trade Name Borsoft™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Borsoft™ SD200CF High Impact Polypropylene Random Heterophasic Copolymer for Cast Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Borsoft SD200CF is a very soft random heterophasic copolymer, suitable for use on chill roll process. The product combines unique softness with outstanding mechanical properties making it the ideal solution for mono and coex film design.Borsoft SD200CF is especially suitable for stationery folders, food/textile packaging, technical films, property modification in other applications fields, substitution of other plastics, and hygienic filmsInformation provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.900 - 0.910 g/cc
0.0325 - 0.0329 lb/in³
ISO 1183
Thickness 50.0 microns
1.97 mil
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 650 %
650 %
ISO 527-3
Film Elongation at Break, TD 850 %
850 %
ISO 527-3
Flexural Modulus 0.450 GPa
65.3 ksi
ISO 178
Secant Modulus, MD 0.200 GPa
29.0 ksi
ISO 527-3
Secant Modulus, TD 0.300 GPa
43.5 ksi
ISO 527-3
Impact 57.5
57.5
Dynatest, Damaging Force (N); ISO 7765-2
Impact Test 1.60 J
1.18 ft-lb
Dynatest, Penetration Energy; ISO 7765-2
Film Tensile Strength at Break, MD 30.0 - 50.0 MPa
4350 - 7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 - 45.0 MPa
3630 - 6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 140 - 144 °C
284 - 291 °F
ISO 3146
Vicat Softening Point 115 °C
239 °F
A (10N); ISO 306
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM D1003
<= 8.0 %
<= 8.0 %
ASTM D1003
Gloss >= 20 %
>= 20 %
ASTM D2457