DuPont Performance Polymers Delrin® FG150 NC010 Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® FG150 NC010 Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High Viscosity Acetal Homopolymer Developed for Food Contact ApplicationsDelrin FG150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has low die deposit and low porosity. It has been developed for consideration in applicationsInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.018 cm/cm	0.018 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.020 cm/cm	0.020 in/in	ISO 294-4 2577
Melt Flow	1.9 g/10 min @Load 2.16 kg, Temperature 190 °C	1.9 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133
	2.4 g/10 min @Load 2.16 kg, Temperature 190 °C	2.4 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	72.0 MPa	10400 psi	ISO 527-1/-2
Elongation at Break	40 %	40 %	Nominal; ISO 527-1/-2
Elongation at Yield	22 %	22 %	ISO 527-1/-2
Tensile Modulus	3.10 GPa	450 ksi	ISO 527-1/-2
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/m²	4.76 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²	ISO 179/1eA
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 µm/m-°C	61.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	97.0 °C	207 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10

Descriptive Properties	Value	Comments
Additives	Release agent
Delivery Form	Pellets
Part Marking Code	>POM<	ISO 11469
Processing	Injection Moulding
	Other Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM	ISO 1043
UL recognition	UL