- Arlon 30400N125 0.125" (3.17 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
Arlon 30400N125 0.125" (3.17 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
| Category | Polymer , Thermoset , Silicone , Silicone Rubber |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 30400N125 0.125" (3.17 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Uncured Unsupported Silicone Rubber on a Kodacel Carrier Appearance: Translucent silicone rubber on polymer linerThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene Interleave |
| 127 microns | 5.00 mil | Kodacel Substrate | |
| 2870 - 3480 microns | 113 - 137 mil | Overall | |
| 2870 - 3480 microns | 113 - 137 mil | Side 1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 - 60 | 50 - 60 | Compound Property |
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Elongation at Break | >= 500 % | >= 500 % | Compound Property |
| 100% Modulus | >= 0.00172 GPa | >= 0.250 ksi | |
| Tear Strength | >= 35.1 kN/m | >= 200 pli | Compound Property |
| Compression Set | <= 28 % | <= 28 % | After Post Cure, Compound Property |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 177 °C |
0.500 hour @Temperature 350 °F |
Recommended Cure Cycle |
| 240 min @Temperature 227 °C |
4.00 hour @Temperature 440 °F |
Recommended Postcure Cycle | |
| Shelf Life | 3.00 Month @Temperature 4.44 °C |
3.00 Month @Temperature 40.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Naturally Translucent | |
| Total Product Weight (oz/yd2) | 103.5 - 132.5 |