Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 6.896 MPa @Temperature 100 °C, Time 346000 sec |
1000 psi @Temperature 212 °F, Time 96.0 hour |
Oil Aged |
S&E Specialty Polymers TufGuard E™ XP-115DD-Zeta PE, Flame Retardant Application: Chlorinated PE TPO based compound suitable for Wire and Cable applications.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Garlock 2103 C.I. SBR/NBR Sheet Rubber, Polyester Insert Garlock cloth-inserted materials are designed to add stability where mechanical fastening is necessary, and to reduce gasket creep where heavy flange loading is required.Style #2103 C.I. is a smooth.. |
|||
Tensile Strength | 6.89 - 20.7 MPa | 1000 - 3000 psi | ASTM D638, ASTM D1709 |
Garlock 9405 PTFE Rubber Sheet, 25% Glass Filled Premium Grade 25% Glass-filled Skived PTFE SheetInformation provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Typical |
Garlock Bay State 22 Natural/SBR Sheet Rubber Blend of natural and SBR rubber, specially compounded to be quick-sealing, non-hardening and heat resistant.Red, smooth rotocured finish. It conforms easily to uneven flange surfaces.Information pr.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | across grain; ASTM F152 |
Garlock MULTI-SWELLâ„¢ 3760 Compressed Aramid Fiber Gasketing Aramid fibers with a proprietary rubber binder.Creates compressive load in light weight flanges in oil and water serviceTwice as compressible as standard fiber gasketsSeals with low load and irregul.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
Garlock 8314 EPDM Sheet Rubber Gasketing Ethylene Propylene Diene Monomer (EPDM)Resists weathering, ozone, and UV exposure.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM F152 |
Garlock 9518 Fluoroelastomer Sheet Rubber Gasketing Fluoroelastomer (FKM) Type AExceptional resistance to heat, oils, fuels, numerous acids, and many other chemicals.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412-98 |
Saint-Gobain Tygon® Norprene® A-60-F I.B. Pressure Tubing Formulation for CIP and SIP cleaning and sterilization systems Good for use in clean-in-place and steam-in-place cleaning and sterilization systems, Norprene® Pressure Tubing has excellent alkali resistance and is compatible with numerous oxidizing agents su.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412 |
Teknor Apex Telcar® OBC 2419C Thermoplastic Elastomer Notes: Telcar OBC has superior mechanical strength and higher elongation which will provide a tougher more durable finished product. Telcar OBC can be used in less demanding sealing applications. T.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Arlon 10842N125 Cured/Post-cured, Unsupported Silicone Rubber Low ModulusProduct Color: Natural (Transparent)Interleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Inform.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Arlon 10842R125 Cured/Post-cured, Unsupported Silicone Rubber Low ModulusProduct Color: RedInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by .. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 10842S060 0.060" (1.52 mm) Fully Cured, Unsupported, Silicone Rubber Design/Construction:Side 1: Fully Cured, Unsupported, Silicone Rubber Appearance: Dark red silicone rubberThis data represents typical values for the production material. The data should not be used.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | |
Arlon 10842S090 Fully Cured, Unsupported Silicone Rubber Product Color: Saddle BrownInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by AR.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property |
Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Prime Coated 1523 FiberglassSide 2: Uncured Silicone RubberInterleave: 0.003" PolyethyleneThis data represents typical values for the .. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; Arlon SQA-TMS-008 |
Arlon 25188T020 0.020" Uncured Silicone Rubber/Laminated ETFE Film Design/Construction:Liner: 0.003" PTFE Coated FiberglassSide 1: Uncured Silicone RubberSubstrate: Laminated ETFE Film-treated for adhesionThis data represents typical values for the production ma.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 30400N085 0.085" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon 48366X007 0.007" (0.178 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1080 FiberglassSide 2: Uncured Silicone RubberInterleave: Polyethylene This data represents typical values for the production mater.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 55949C028W 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber LayerSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in pl.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon R30711R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave 1: PolyethyleneSide 1: Uncured Silicone Rubber Substrate: Style 1165 Fiberglass Side 2: Uncured Silicone Rubber Interleave 2: PolyethyleneAppearance: Red silicone gum .. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Silicone Property |
Arlon 30850S125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property |
Arlon 41940C020 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured, Unsupported Silicone RubberSubstrate: Holland Cloth CarrierThis data represents typical values for the production material and .. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon 48362X005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1080 FiberglassProduct Use: Flexible hose/duct substrateAppearance: Gray silicone rubber on fiberglass fabricThis data represents t.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 51946C015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 55949C028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber LayerSide 2: Uncured Silicone Rubber Appearance: Brown silicone rubber and gum on fiberglass clothThis data Represents typical values for the produc.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | ASTM D412 |
Arlon 910-10W##-P0 0.010" (0.254 mm) Cured Self-fusing Silicone Tape Design/Construction: Interleave: Polyethylene Rubber: Cured Self-fusing Silicone Rubber Cross Section Type: 1” Wide Rectangular 1 inch wide, 10 mil thick, White, Rectangular cross-section, Self-fu.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon R33670N004 0.004" (0.102 mm) Uncured Silicone Rubber with K2030 PEN Film Substrate Design/Construction:Side 1: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Inf.. |
|||
Tensile Strength | 6.89 - 8.27 MPa | 1000 - 1200 psi | Compound Property |
Arlon R33682C045 0.045" (1.14 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Infor.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon R34260N005 0.005" (0.127 mm) Unsupported/Uncured Rubber with Fiberglass Substrate Design/Construction:Side 1: Unsupported/Uncured Rubber Appearance: Clear gum on release linersThis data Represents typical values for the production material. The data should not be used to write, o.. |
|||
Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
Arlon 44686W013 0.013" (0.330 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone Rubber UL Recognition: 220°C per UL Card E54153Appearance: White silicone gum on fiberglassThis data represents typical val.. |
|||
Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 |
Arlon 43362X0055 0.0055" (0.140 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 1: Cured Silicone RubberSubstrate: Style 2112 FiberglassFlame Resistance: Product meets Title 14 CFR 25.856(a) Appendix F, Part VI (amdt. 25-111) fl.. |