- Aremco Aremco-Bond™ 2300 High Performance Epoxide
Aremco Aremco-Bond™ 2300 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2300 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Milky Clear, 10:1, Low Viscosity, Exceptional Bond Strength.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | |
| Viscosity | 5000 cP | 5000 cP | Mixed Viscosity |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Shear Strength | 31.4 MPa | 4560 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 66.6 µm/m-°C @Temperature 20.0 °C |
37.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 177 °C | 350 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.30 % | 0.30 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
|
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | |
| Dissipation Factor | 0.0080 | 0.0080 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 65.6 °C |
2.00 hour @Temperature 150 °F |
Recommended Cure |
| 2880 min @Temperature 23.0 °C |
48.0 hour @Temperature 73.4 °F |
Alternate Cure | |
| Pot Life | 45.0 min @Temperature 25.0 °C |
45.0 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Very Good | |
| Color | Milky Clear | |
| Mix Ratio By Weight | 100:10 | resin:hardener |
Users viewing this material also viewed the following:
- PolyOne Dynalloy™ OBC 8100-N65 Thermoplastic Elastomer (TPE)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Monoplex DOS Plasticizer
- Kolon SPESIN® KP213G30SB3 Glass Fiber Reinforced PBT Compound Resin
- LATI Larton GCE/600 PPS, Glass/Mineral Reinforced
- SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East)
- A. Schulman POLYTROPE™ TPP 518 Injection Grade Olefinic Thermoplastic Elastomer
- Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI)
- Braskem LQ 0518/30 LLDPE Blown Film Extrusion Polyethylene
- BASF Elastollan® C-64D Polyester Type Polyurethane Elastomer
- Gouda Vuurvast CURON 165 Dense Refractory Castable
Copyright © lookpolymers.com All Rights Reserved