Aclo Accutech Polycarbonate POL050G20L Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polycarbonate POL050G20L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 95.98 MPa | 13920 psi | ASTM D638 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.900 GPa | 565.6 ksi | ASTM D638 |
| Flexural Strength | 164.0 MPa | 23780 psi | ASTM D790 |
| Flexural Modulus | 5.899 GPa | 855.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F |