Polymer Property : Tensile Strength, Yield = 100 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP66GF13 Nylon 66, 13% Glass Reinforced Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared..
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ASTM D638
Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced Glass reinforced (13 %) High Temperature Polyamide - Blow Molding grade with excellent chemical resistance, improved flow and high HDT. *All properties are measured after 48 hours of conditioning at..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Oxford Polymers 901-BK Polycarbonate/Polyetherimide Alloy Polycarbonate/Polyetherimide AlloyInformation provided by Oxford Polymers.
Tensile Strength, Yield	100 MPa	14500 psi	Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
PolyOne Edgetek® PK-1000 Polyetheretherketone (PEEK) (discontinued **) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM-D638
Polyram PE322G22 PET, 22% Glass Fiber (discontinued **) 22% Glass fiber reinforced, flame retardant PET for injection molding applications.Information provided by Polyram Ram On Ind.
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527
Victrex® PEEK 150PF Easy Flow Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression molding, easy flow, FDA food contact compliant, ..
Tensile Strength, Yield	100 MPa	14500 psi	Result based on similar products; ISO 527
Victrex® PEEK 150UF10 Polyetheretherketone Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for composite manufacture, easy flow, FDA food contact compliant..
Tensile Strength, Yield	100 MPa @Temperature -40.0 °C	14500 psi @Temperature -40.0 °F	ISO 527
BASF Capron® 8224 HSL Nylon 6 (Conditioned) (discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
FiberfilÂ® J-69/30/E High performance polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics
Tensile Strength, Yield	100 MPa	14500 psi	2.0 in/min; ASTM D638
LTL Color Compounds ColorFastÂ® PCGF130 Polycarbonate, 30% Glass-Filled 30% glass-filled grade polycarbonateAll information provided by LTL Color Compounders, Inc.
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Lucent Polymers G66-13 Nylon 66, 13% Glass Fiber Reinforced Add "H" for Heat Stabilized Add "HU" for WeatherableTypical Properties, Dry as MoldedInformation provided by Lucent Polymers, Inc.
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® A 230 V13 PA66, 13% glass fiber, DRY Description: Modified polyamide 66, reinforced with 13% of glass fiber, with improved impact resistance, for injection molding.Available in: Europe and North AmericaProduct Applications: In addition..
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® A 238 V13 PA66, 13% glass fiber, DRY Description: Polyamide 66, reinforced with 13% of glass fiber, heat stabilized, with improved impact resistance, for injection molding.Available in: Europe, Latin America and North AmericaProduct Ap..
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM CRS5011R PEI Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant.
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM UF5011S PEI (Asia Pacific) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET (Asia Pacific) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® DR48 PBT (Europe-Africa-Middle East) VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromoto..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Techmer ES LuriblendÂ® PA4/6 HS L BK Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedUL File Number: E157318Appearance: BlackInformation provided by TP Composites..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Techmer ES PlastiblendÂ® TPX-HTN-000BB Availability: North AmericaForms: Pellets Features: High Heat ResistanceInformation provided by TP Composites, Inc.
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Washington Penn Homopolymer Polypropylene 40% Glass Reinforced Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. ..
Tensile Strength, Yield	100 MPa	14500 psi
Trelleborg Vamac® E650C Ethylene-Acrylate Rubber PropertiesGood temperature range from -60°C to +175°C constant and up to +200°C intermittently.Excellent resistance to ozone and weathering.At elevated temperatures it exhibits reasonable mechani..
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527
Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized 15% Glass fiber reinforced, impact modified and UV stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527-1/-2
DSM Stanyl® TW441 Nylon 46 (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing unmatched performance and value across an amazingly broad range of automotive and electronic applications. Stanyl offers:Highest mechanical propertie..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Ashley Polymers Ashlene® 742L-13G Nylon 6/66, 13% Glass Reinforced 6/66 Copolymer with high surface gloss in addition to high stiffness and strength, 13% Glass Reinforced.Data provided by the manufacturer
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ISO 527-2
BASF Ultradur® S 4090 G4X 20% Glass Filled PBT Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 20% of glass fibers for industrial parts with high dimensional stab..