3M 1000 NS Fire Barrier Water Tight Sealants

Category Other Engineering Material
Manufacturer 3M
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M 1000 NS Fire Barrier Water Tight Sealants.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M Fire Barrier Water Tight Sealants 1000 NS and 1003 SL are ready-to-use, single component, neutral cure, silicone sealants that cure upon exposure to atmospheric humidity to form a flexible firestop seal. This material helps control the spread of fire, smoke and noxious gasses before, during and after exposure to a fire when installed in accordance with a listed through penetration or fire-resistive joint assembly. 3M Fire Barrier Water Tight Sealants 1000 NS is a non-slump firestop used primarily on vertical surfaces with 3M Fire Barrier Water Tight Sealant 1003 SL is a self-leveling firestop ideal for floor applications. These firestop sealants also meets UL Water Leakage Test, W Rating – Class 1 requirements for systems tested and listed in accordance with ANSI/UL 1479. Both products are elastomeric, are ready-to-use and exhibit excellent weatherability.Information provided by 3M
Physical Properties Metric English Comments
Volatile Organic Compounds (VOC) Content <= 250 g/l
<= 250 g/l
VOC Less H2O and Exempt Solvents
Mechanical Properties Metric English Comments
Hardness, Shore A 20 - 25
20 - 25
ASTM C66
Tensile Strength at Break 0.590 MPa
85.6 psi
Elongation at Break 600 %
600 %
ASTM D412
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 149 °C
300 °F
Minimum Service Temperature, Air -51.0 °C
-59.8 °F
Processing Properties Metric English Comments
Cure Time 10.0 min
0.167 hour
Tack free, RT @ 50%RH
30.0 - 60.0 min
0.500 - 1.00 hour
Dry to touch, RT @ 50%RH
Shelf Life 4.00 - 32.0 Month
4.00 - 32.0 Month
Descriptive Properties Value Comments
Appearance Light Gray