Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | working strength |
Permabond TA436 Toughened Acrylic Adhesive PERMABOND TA436 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. Permabond TA436 is a no-mix system which obtains handling strength.. |
|||
Cure Time | 3.00 - 60.0 min @Temperature 60.0 - 170 °C |
0.0500 - 1.00 hour @Temperature 140 - 338 °F |
Average value: 25.8 min Grade Count:12 |
Overview of materials for Cyanoacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Cyanoacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Ambient |
Reltek BONDiT™ A-43 Bonding Agent, Primer and Adhesive Key Properties: Adhesion promoter for most thermoplastics, thermoset materials, elastomers, polyurethanes.Can be used on metals, glass and ceramicApplications: High functionality produces good bond .. |
|||
Cure Time | 10.0 - 60.0 min | 0.167 - 1.00 hour | Average value: 21.3 min Grade Count:6 |
Overview of materials for Silicone Foam This property data is a summary of similar materials in the MatWeb database for the category "Silicone Foam". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Cure Time | 15.0 - 60.0 min @Temperature 23.0 °C |
0.250 - 1.00 hour @Temperature 73.4 °F |
|
Humiseal 1C65 Silicone Conformal Coating Humiseal 1C65 Silicone Conformal CoatingHigh temperature resistanceGood dielectrical propertiesGood moisture resistanceRepairableUL Approval PendingMIL-I-46058C Approval PendingPasses thermal shock .. |
|||
Cure Time | 45.0 - 60.0 min @Temperature 60.0 °C |
0.750 - 1.00 hour @Temperature 140 °F |
Full cure in 45 to 60 mins at 140°F. |
Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive Description:#1101 is a light grayish-tan two part epoxy adhesive that was developed especially for difficult bonding problems involving similar or dissimilar materials. #1101 provides excellent adhe.. |
|||
Cure Time | 30.0 - 60.0 min @Temperature 125 °C |
0.500 - 1.00 hour @Temperature 257 °F |
|
Lord Adhesives Thermosetâ„¢ MS-330 Silicone Board Level Encapsulant LORD Thermosetâ„¢ MS-330 encapsulant is a one component silicone specifically designed for use on high-frequency devices including Bluetooth applications. This silicone encapsulant offers excelle.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Functional cure |
ITW Devcon 5 minute® Epoxy Gel, Opaque Information provided by ITW Devcon |
|||
Cure Time | 30.0 - 60.0 min @Temperature 150 °C |
0.500 - 1.00 hour @Temperature 302 °F |
|
Gwent Electronic Materials C2050425D1 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and .. |
|||
Cure Time | 9.00 - 60.0 min | 0.150 - 1.00 hour | |
Master Bond Supreme 10AOHT-LO High Shear and Peel Strength Epoxy Description: Master Bond Supreme 10AOHT-LO has a combination of properties consisting of excellent thermal conductivity, superior electrical insulation, great adhesion to a wide variety of substrate.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | |
Trelleborg Emerson & Cuming Stycast® 1090/11 Two-Component General Purpose Encapsulant Features and Typical Applications: Designed as general purpose encapsulants, these products offer a wide range of features including thermal conductivity, mechanical shock and impact resistance, as .. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | |
Trelleborg Emerson & Cuming Stycast® 2850FT-FR/11 Two-Component Epoxy Flame Retardant Encapsulant Features and Typical ApplicationsProvide flame resistance down to 1/8 of an inch. These products also offer various other features such as thermal shock protection, low viscosity, and thermal conduc.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Dry to touch, RT @ 50%RH |
3M 1000 NS Fire Barrier Water Tight Sealants 3M Fire Barrier Water Tight Sealants 1000 NS and 1003 SL are ready-to-use, single component, neutral cure, silicone sealants that cure upon exposure to atmospheric humidity to form a flexible firest.. |
|||
Cure Time | 40.0 - 60.0 min | 0.667 - 1.00 hour | Tack-Free, 50% RH |
3M 740 Hybrid Sealant 3M™ 700-Series Hybrid Sealant and Hybrid Adhesive Sealant products are one component, moisture curing products which form permanent elastic bonds. They are similar in function as a typical one comp.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Dry to touch, RT @ 50%RH |
3M IC 15WB+ Fire Barrier Sealant 3M Fire Barrier Sealant IC 15WB+ is a cost-effective, one-part, gun-grade, latex-based, intumescent firestop sealant that dries to form a monolithic firestop seal that also acts as a barrier to airb.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM 118 QSI Quantum Silicones 18 Durometer Condensation Cured Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is an.. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material QM 122 is a two-component, room temperature condensation cure silicone material. The cured rubber is flexible with excellent mechanical and physical properties in addition to good shelf-life stabili.. |
|||
Cure Time | 20.0 - 60.0 min @Temperature 24.0 °C |
0.333 - 1.00 hour @Temperature 75.2 °F |
|
BCC Products BC 4544 Polyester Carvable Wood Filler This polyester resin base compound is easy to use, sets in minutes and can be sanded or carved almost immediately. Acts like wood yet exhibits no grain problems. BC4544 Wood Filler can be carved, sa.. |
|||
Cure Time | 20.0 - 60.0 min @Temperature 24.0 °C |
0.333 - 1.00 hour @Temperature 75.2 °F |
|
BCC Products BC 4553 Polyester Styling Paste BC4553 is designed for instant buildup and repair of plastic surfaces and models. Recommended for use on SMC and FRP parts, vacuum form molds and a variety of surfaces. When cured BC4553 produces a .. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Touch Dry |
3M Scotchkote™ XF 895 Fast Curing Floor Coating Scotchkote Fast Curing Floor Coating XF 895 has been specifically developed as a high build floor protection system for application to concrete surfaces, to provide rapid return to serviceProduct Fe.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | at 200°F; 0.75-1 hr at 480°F |
Aremco Aremco-Seal™ 529 High Temperature Specialty Coatings Silicone Transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Air Set prior to curing |
Aremco Aremco-Seal™ 529VHV High Temperature Specialty Coatings Silicone Very high viscosity version, transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Air Set prior to curing |
Aremco Aremco-Seal™ 613 High Temperature Specialty Coatings Glass |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | Dry to touch, RT @ 50%RH |
3M FD 150+ Fire Barrier Sealant 3M Fire Barrier Sealant FD 150+ is an economical, ready to use, gun-grade, elastomeric sealant that dries to from a monolithic flexible firestop seal. 3M Fire Barrier Sealant FD 150+ firestops joint.. |
|||
Cure Time | 30.0 - 60.0 min | 0.500 - 1.00 hour | at 200°F; 0.75-1 hr at 480°F |
Aremco Aremco-Seal™ 529HV High Temperature Specialty Coatings Silicone High viscosity version, transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters. |
|||
Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Tack Free Time, catalyzed with QM CAT RED 3 |
ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material QM 113 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is an.. |
|||
Cure Time | 30.0 - 60.0 min @Temperature 90.0 °C |
0.500 - 1.00 hour @Temperature 194 °F |
|
Gwent Electronic Materials C2040226D2 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and .. |
|||
Cure Time | 30.0 - 60.0 min @Temperature 90.0 °C |
0.500 - 1.00 hour @Temperature 194 °F |
|
Gwent Electronic Materials C2040226D4 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and .. |