Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Network Polymers MS 200 Styrene Methyl Methacrylate Copolymer Description: Styrene Methyl Methacrylate CopolymerInformation provided by Network Polymers Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ 80510 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ 80520 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ 81510 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Nilit Polynil® P60 Medium Viscosity Nylon 66 Description: Polynil P60 is a grade has a viscosity that has been optimized for monofilament extrusion.Key characteristics: Viscosity number 155 gr/cm3Excellent melt stabilityHigh elongationInformat.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ 80530 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 - 93.9 °C | 169 - 201 °F | Average value: 82.0 °C Grade Count:9 |
Overview of materials for Acrylic, High Flow, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, High Flow, Molded". Each property range of values reported is minimum and maximum values of app.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
I. Stern HIPS SH03 High Impact Polystyrene Features:High flowExcellent toughnessExcellent processabilityApplicationsInjection moldingAgency RatingsFDA Title 21 CFR 177.1640UL File E185934Information provided by I. Stern & Co. Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Shuman 710H Utility Black ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Shuman 720H Black ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Shuman 730 Utility White ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Shuman 730H White ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
Shuman 780H Grey ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® ABS LG UV Availability: North AmericaForms: PelletsFeatures: Low GlossInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Diamond Polymers ABS 9500B Description: Blow Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Diamond Polymers ABS 9501 Description: Injection Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Diamond Polymers ABS 9502 Description: Injection Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
Diamond Polymers ABS 9502E Description: Extrusion Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | |
Aclo Accucomp ABS ABS827L Electroplating Grade |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 - 203 °C | 169 - 397 °F | Average value: 94.0 °C Grade Count:25 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 76.1 - 98.9 °C | 169 - 210 °F | Average value: 91.9 °C Grade Count:4 |
Overview of materials for Styrene/Methyl Methacrylate Copolymer (SMMA) This property data is a summary of similar materials in the MatWeb database for the category "Styrene/Methyl Methacrylate Copolymer (SMMA)". Each property range of values reported is minimum and max.. |