PolyOne Geon™ 80510 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ 80510 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Spiral Flow | 88.9 cm | 35.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | ASTM D2240 |
| Tensile Strength, Yield | 62.1 MPa | 9010 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Poissons Ratio | 0.44 | 0.44 | ASTM E132 |
| Shear Modulus | 1.44 GPa | 209 ksi | Calculated |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Izod Impact, Unnotched | 4.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
8.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
ALL; UL 94 |
| V-0 @Thickness 1.63 mm |
V-0 @Thickness 0.0642 in |
All Colors | |
| 5VA @Thickness 1.47 mm |
5VA @Thickness 0.0579 in |
ALL; UL 94 | |
| 5VA @Thickness 1.63 mm |
5VA @Thickness 0.0642 in |
All Colors |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| High Flow | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 10% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Appliances | |
| Business Equipment | ||
| Construction Applications | ||
| Electrical/Electronic Applications | ||
| General Purpose |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML3982 PC (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 1105-8179 PEEK, with carbon fiber
- SABIC Innovative Plastics LNP THERMOCOMP AF003 ABS
- Styrolution Novodur® 595CP ABS
- ChevronTexaco CP Grease
- 3M Dyneon™ PFA 6910GZ Fluoroplastic Dispersion
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N220 Filler
- Ashley Polymers Ashlene® P291WO PPO
- LTL Color Compounds ColorFast® NY2 Nylon 66
Copyright © lookpolymers.com All Rights Reserved