SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.620 % | 0.620 % | 50% RH, 24 hrs; ASTM D570 |
| 0.990 % | 0.990 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 91.0 MPa | 13200 psi | Type I, 5 mm/min; ASTM D638 |
| 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | Type I, 5 mm/min; ASTM D638 |
| 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.01 GPa | 1160 ksi | 1 mm/min; ISO 527 |
| 8.92 GPa | 1290 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 134 MPa | 19400 psi | ISO 178 |
| 179 MPa | 26000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.33 GPa | 918 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.63 GPa | 962 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.91 J/cm | 5.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.67 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 8.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D257 |