SABIC Innovative Plastics LNP STAT-KON RE0039 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RE0039 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* RE0039 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ASTM D792
Moisture Absorption 0.550 %
0.550 %
50% RH, 24 hrs; ASTM D570
0.870 %
0.870 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0017 - 0.0026 cm/cm

@Time 86400 sec
0.0017 - 0.0026 in/in

@Time 24.0 hour
ISO 294
0.0020 - 0.0030 cm/cm

@Time 86400 sec
0.0020 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0068 - 0.0078 cm/cm

@Time 86400 sec
0.0068 - 0.0078 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0080 cm/cm

@Time 86400 sec
0.0070 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 205 MPa
29700 psi
ASTM D638
209 MPa
30300 psi
ISO 527
Elongation at Break 2.2 %
2.2 %
ASTM D638
2.2 %
2.2 %
ISO 527
Tensile Modulus 15.6 GPa
2260 ksi
1 mm/min; ISO 527
17.58 GPa
2550 ksi
50 mm/min; ASTM D638
Flexural Strength 297 MPa
43100 psi
ASTM D790
318 MPa
46100 psi
ISO 178
Flexural Modulus 11.44 GPa
1659 ksi
ASTM D790
14.2 GPa
2060 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.04 J/cm
13.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
25.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
45.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
25.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
66.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 228 °C
442 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
247 °C

@Thickness 3.20 mm
477 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257