Solvay TECHNYL® A 218W V33 Natural T PA66, 33% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218W V33 Natural T PA66, 33% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 218W V33 Nat T is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The product is particularly recommended for the molding of parts where some translucency is required, as well as surface aesthetics is important.Available in: North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This grade is particularly recommended for the injection molding of parts in permanent contact with cooling liquids in cars, such as reservoir bottles.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183/A
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ISO 527 Type 1A
Tensile Stress 25.0 MPa

@Strain 1.00 %,
Temperature 150 °C
 3630 psi

@Strain 1.00 %,
Temperature 302 °F
35.0 MPa

@Strain 1.00 %,
Temperature 100 °C
 5080 psi

@Strain 1.00 %,
Temperature 212 °F
45.0 MPa

@Strain 2.00 %,
Temperature 150 °C
 6530 psi

@Strain 2.00 %,
Temperature 302 °F
55.0 MPa

@Strain 3.00 %,
Temperature 150 °C
 7980 psi

@Strain 3.00 %,
Temperature 302 °F
60.0 MPa

@Strain 2.00 %,
Temperature 100 °C
 8700 psi

@Strain 2.00 %,
Temperature 212 °F
60.0 MPa

@Strain 4.00 %,
Temperature 150 °C
 8700 psi

@Strain 4.00 %,
Temperature 302 °F
70.0 MPa

@Strain 6.00 %,
Temperature 150 °C
 10200 psi

@Strain 6.00 %,
Temperature 302 °F
75.0 MPa

@Strain 10.0 %,
Temperature 150 °C
 10900 psi

@Strain 10.0 %,
Temperature 302 °F
80.0 MPa

@Strain 3.00 %,
Temperature 100 °C
 11600 psi

@Strain 3.00 %,
Temperature 212 °F
85.0 MPa

@Strain 4.00 %,
Temperature 100 °C
 12300 psi

@Strain 4.00 %,
Temperature 212 °F
90.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 13100 psi

@Strain 1.00 %,
Temperature 73.4 °F
95.0 MPa

@Strain 6.00 %,
Temperature 100 °C
 13800 psi

@Strain 6.00 %,
Temperature 212 °F
100 MPa

@Strain 10.0 %,
Temperature 100 °C
 14500 psi

@Strain 10.0 %,
Temperature 212 °F
105 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 15200 psi

@Strain 1.00 %,
Temperature -40.0 °F
155 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 22500 psi

@Strain 2.00 %,
Temperature 73.4 °F
180 MPa

@Strain 2.00 %,
Temperature -40.0 °C
 26100 psi

@Strain 2.00 %,
Temperature -40.0 °F
180 MPa

@Strain 3.00 %,
Temperature 23.0 °C
 26100 psi

@Strain 3.00 %,
Temperature 73.4 °F
220 MPa

@Strain 3.00 %,
Temperature -40.0 °C
 31900 psi

@Strain 3.00 %,
Temperature -40.0 °F
Elongation at Break 3.8 %
3.8 %
ISO 527 Type 1A
Tensile Modulus 10.2 GPa
1480 ksi
ISO 527 Type 1A
Flexural Strength 294 MPa
42600 psi
ISO 178
Flexural Modulus 8.95 GPa
1300 ksi
ISO 178
Izod Impact, Notched (ISO) 11.3 kJ/m²
5.38 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 9.07 J/cm²
43.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -40.0 °C
 4.28 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA
1.10 J/cm²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 247 °C
477 °F
ISO 75/Af
Processing Properties Metric English Comments
Feed Temperature 255 - 265 °C
491 - 509 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 265-275°C
Mixing Zone 275-280°C