Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 437 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific)
Thermoplastic Polyimide Extem* XH1005 Resin.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Europe-Africa-Middle East)
Thermoplastic Polyimide Extem* XH1005 Resin.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Ravago Manufacturing Americas Enviramid™ N1335HL BK Post Consumer Recycle Nylon 66, 35% Glass Filled
Heat Stabilized, Lubricated, Black, and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
LATI LAESTRA E01 G/30 30% Glass Fiber Reinforced, Elastomer Modified Syndiotactic Polystyrene (SPS)  (disconti
Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75
Nilit FRIANYL C73 GV40 Nylon 6.6/6 for injection molding, 40% glass fiber reinforced
Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Deflection Temperature at 1.8 MPa (264 psi) 225 °C

@Thickness 6.40 mm
437 °F

@Thickness 0.252 in
ASTM D648
Kingfa PET-RG30 Flame Retardant, 30% Glass Fiber Reinforced PET
Features:Flame retardantHigh strengthGood heat resistanceOutstanding electrical propertiesApplications:Injection moldingConnectorsRelayBobbinsSocketsE & E partsInformation Provided by Kingfa Sci. & ..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFL369 PA6.6 (Europe-Africa-Middle East)
LNP* LUBRICOMP* RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricated
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Shinkong Synthetic Fibers Shinite® F602G30 Nylon 66, 30% Glass Filled, Fire Retardant, Halogen Free
Information from Shinkong Synthetic Fibers Corp.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Plastics Group Polifil® 71MR Mineral-Reinforced Nylon 6/6 (DAM)
Polifil® GFN/MRN 6/6 reinforced series of compounds offer superior strength, rigidity and creep resistance. Glass fibers provide excellent thermal and dimensional stability while maintaining good h..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-1/-2
Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Dry
Information provided by Unitika Ltd.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75
Polyram RamLloy A300NT Nylon 66/Polypropylene Alloy, 30% Glass Fiber Reinforced
Nylon 66/PP alloy 30% glass fiber reinforced for injection molding applications.Information provided by Polyram.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-93
Wellman Wellamid® GF1662-GY1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6
Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75
Wellman Wellamid® GF43-66/6 XE-N 43% Glass Fiber Reinforced Nylon 66/6, Lubricated & Heat Stabilized
Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-93
Wellman Wellamid® GF43-66/6 XE-NBK1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6
Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-93
Wellman Wellamid® GFX1743-N1(PTFE) 45% Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6
Description: Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6Information provided by Wellman.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-93
Wellman Wellamid® MRGF25/25 22H-NBK1 Nylon 66, 25% Mineral and 25% Glass Reinforced
All information provided by Wellman Engineered Resins.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Toyobo Vylopet® EMC145 Glass Reinforced Polyester, Standard Grade
Key Feature: Flame retardant V-0 UL-94 classApplications: Ultra-precise componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and trac..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Toyobo VYLOPET® EMC333 Injection Molding Polyester Resin, Hydrolysis Resistant
Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo.
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-1/-2
EMS-Grivory Grivory® TSG-25/4 PA666-GF25
Information provided by EMS Grivory
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-1/-2
EMS-Grivory Grivory® TSGZ-15/4 PA666-GF15
Information provided by EMS Grivory
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75
Eurotec® Tecopet® PT70 GR30 NL100 XD70 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), long-term heat stabilized, natural
Information provided by Eurotec®
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75
Eurotec® Tecopet® PT74 GR45 BK002 PR PET, 45% glass fiber reinforced, high heat stabilized, black
Information provided by Eurotec®
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Arkema Group Orgalloy® RS 6630 Nylon 66 Alloy, 30% Glass Fiber (Conditioned)
RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
HDT/A; ISO 75-1/2
Akro-Plastic Akroloy® PA GF 60 (2844) PA 6.6 & PA6I/6T Dry, 60% Glass Filled
One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-1, -2
Celanese VECTRA E531i LCP, 30% Mineral Reinforced
Mineral filled grade with low warp, easy flow and smooth surface appearance.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-2
BASF Ultrason® E 2010 C6 30% Carbon Filled
Carbon fibers and Ultrason® two partners with good properties. The combination of carbon fibers with the amorphous high-temperature plastic Ultrason® guarantees mechanical properties for temperatu..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ISO 75-1, -2
Celanese IMPET 2700 GV1/30 PET, 30% Glass Reinforced
30% glass filled Polyethylene terephthalate (PET) with high flowability, excellent gloss, high modulus, and high heat deflection temperature.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
LATI Latamid 66 H2 G/25-V0KB3 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
ASTM D648
Covestro Petlon® 3530 Semi-Crystalline PET, 30% Glass Fiber  (discontinued **)
Characteristics: Excellent Electrical Properties, High Heat and Chemical ResistanceApplications: Automotive (Underhood), Appliances, Casings and HousingsProcessing: Injection Molding (Melt Temperatu..
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Verton WV00A PBT (Europe-Africa-Middle East)
LNP VERTON* WV00A is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.