Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 225 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	STN EN ISO 75-2 (A)
Plastcom SLOVAMID® 6 GF 20 FRA 5 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 20% glass fiber, flame retarded with halogen flame retardant. Main features: flammability in accordance with UL 94 5 at 1.6 mm, glow wire at 960°C. Appli..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1005 Resin.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75
Nilit FRIANYL C73 GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	Unannealed; ASTM D648
Ravago Manufacturing Americas Enviramid™ N1335HL BK Nylon 6/6 Available in North America Filler: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedContains Recycled ContentRoHS Compl..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ASTM D648
Gharda Chemicals Gafone™ T6500 Polysupersulfone (PSS) (discontinued **) Characteristics: Excellent Dimensional Properties Transparent High Mechanical Properties Good Electrical Properties High Tg of 270°C and expected Continuous Use Temperature of 220°C App..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75
Wellman Wellamid® GFT15N050-N2 15% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® 74G33W NC010 Nylon 66 (Unverified Data**) Zytel® 74G33W NC010 is a 33% glass reinforced nylon 66 and nylon 6 co-melt resin with improved weatherability.Information provided by DuPont Performance Polymers
Deflection Temperature at 1.8 MPa (264 psi)	225 - 255 °C	437 - 491 °F	Average value: 239 °C Grade Count:12
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Deflection Temperature at 1.8 MPa (264 psi)	225 Â°C	437 Â°F	ISO 75/Af
Solvay TECHNYLÂ® A 230 V13 PA66, 13% glass fiber, DRY Description: Modified polyamide 66, reinforced with 13% of glass fiber, with improved impact resistance, for injection molding.Available in: Europe and North AmericaProduct Applications: In addition..
Deflection Temperature at 1.8 MPa (264 psi)	225 Â°C	437 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFL369 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricated
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75-1/-2
Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75
Wellman Wellamid® GF33-66/6 XE-N 33% Glass Fiber Reinforced Nylon 66/6, Lubricated & Heat Stabilized Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75
Wellman Wellamid® GF60-66/6 XE-N 60% Glass Fiber Reinforced Nylon 66/6, Lubricated & Heat Stabilized Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75-93
Wellman Wellamid® GFX1743-N1(PTFE) 45% Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6 Description: Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6Information provided by Wellman.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ASTM D648
Toyobo VYLOPET® EMC130-20 Injection Molding Polyester Resin, Flame Resistant Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ASTM D648
A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75-1/-2
DSM Arnite® AV2 340 PET-20% Glass Reinforced (European Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame ..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO 75-1/-2
EMS-Grivory Grivory® TSG-25/4 PA666-GF25 Information provided by EMS Grivory
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ASTM D648
E-Polymers Tekaster® F615GFR , Flame Retardant, 30% Glass Reinforced PET 30% Glass Fiber Reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ISO R75
Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6.6 basedMolding of Engineering PartsInformation provided by Arkema Group
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F
Arkema Group Orgalloy® RS 6635 A Nylon 66 Alloy, 35% Glass Fiber (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	HDT/A; ISO 75-1/2
Akro-Plastic Akroloy® PA GF 60 (2844) PA 6.6 & PA6I/6T Dry, 60% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	ASTM Test
BASF Petra® 140 45% Glass Filled PET Petra 140 is a 45% glass reinforced injection molding polyethylene terephthalate (PET) offering an increased level of strength, stiffness, high temperature performance and dimensional stability. Ex..
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	Dry; ASTM D648
Asahi Kasei Leona® 90G50 50% Glass Filled Nylon 66 Enhanced strength and stiffness; with 50% GF. Excellent appearance.Applications:Office furnitureInformation provided by Asahi Kasei
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66 (Unverified Data**) Zytel® 74G33W BK196 is a high gloss automotive weatherable black 33% glass reinforced nylon 66 and nylon 6 comelt resin.Information provided by DuPont Performance Polymers
Deflection Temperature at 1.8 MPa (264 psi)	225 °C	437 °F	DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® 74G33W NC010 Nylon 66 (Unverified Data**) 33% Glass Reinforced UV Stabilized Polyamide 66 + Polyamide 6 Zytel 74G33W NC010 is a 33% glass reinforced nylon 66 and nylon 6 co-melt resin with improved weatherability.Information provided by DuP..