- Shinkong Synthetic Fibers Shinite® F602G30 Nylon 66, 30% Glass Filled, Fire Retardant, Halogen Free
Shinkong Synthetic Fibers Shinite® F602G30 Nylon 66, 30% Glass Filled, Fire Retardant, Halogen Free
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® F602G30 Nylon 66, 30% Glass Filled, Fire Retardant, Halogen Free.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 130.9 MPa | 18990 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 199 MPa | 28900 psi | ASTM D790 |
| Flexural Modulus | 8.66 GPa | 1260 ksi | ASTM D790 |
| Izod Impact, Notched | 0.932 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.74 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7930-9 NSFG Thermoplastic Elastomer (TPE)
- Rochling Engineered Plastics Polystone® Natural (UHMW-PE)
- Karina 800-DA-10/1-A-AT-IS White PVC Compound
- Teknor Apex Monprene® MP-1766-R1 Thermoplastic Elastomer
- A. Schulman PP 1579 Polypropylene Impact Grade Polypropylene
- Williams Advanced Alloys WS292 Solder
- Zotefoams Plastazote® LD33FM Low Density Polyethylene Foam, Flame Retarded
- 3M Dyneon™ FE 5621 Fluoroelastomer
- A. Schulman ComAlloy Comtuf® 621 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced
- LG Chemical LG-604 Styrene-Butadiene-Styrene
Copyright © lookpolymers.com All Rights Reserved