Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 173 - 190 °C | 343 - 374 °F | Average value: 180 °C Grade Count:3 |
Overview of materials for Phenolic, Resole, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Mineral Filled". Each property range of values reported is minimum and maximum values .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 47.0 - 190 °C | 117 - 374 °F | Average value: 75.5 °C Grade Count:26 |
Overview of materials for Nylon 612, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Unreinforced". Each property range of values reported is minimum and maximum values of approp.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit 2923 W Novolac Phenolic Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 54.4 - 190 °C | 130 - 374 °F | Average value: 68.7 °C Grade Count:21 |
Overview of materials for Polybutylene Terephthalate (PBT), PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), PTFE Filled". Each property range of values reported is minimum and ma.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 190 °C | 140 - 374 °F | Average value: 131 °C Grade Count:211 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |