SABIC Innovative Plastics LNP COLORCOMP DX06407H PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP DX06407H PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* DX06407H is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 94 % | 94 % | Type I, 5 mm/min; ASTM D638 |
| 104 % | 104 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.2 % | 6.2 % | Type I, 5 mm/min; ASTM D638 |
| 6.3 % | 6.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.34 GPa | 339 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
| Flexural Modulus | 2.29 GPa | 332 ksi | 2 mm/min; ISO 178 |
| 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.81 J/cm | 14.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.1 J/cm | 24.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 224 kJ/m² | 107 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 63.0 J @Temperature 23.0 °C |
46.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 69.0 J | 50.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 66, Unreinforced
- Shin-Etsu Silicones KE-3421 Silicone, RTV Conformal Coating
- Solvay AG-RHOâ„¢ FKC 1500 Surfactant
- Plastics Group Polifil® GFABS-30 30% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS)
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- A. Schulman LP551-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- Dow Corning XIAMETER® PMCPPMX-200 100CS Silicone Fluid
- E-Polymers SEPAZ® K140HF 40% Glass Fiber Reinforced Low Flash, High Flow PPS Resin
- Supreme Petrochem SP EXP 31 Toughened Polystyrene
Copyright © lookpolymers.com All Rights Reserved