- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 179 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 179 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| Proto3000 Duraform® GF Selective Laser Sintering (SLS®) Prototyping Polymer Description: Glass-filled polyamide (nylon) material for real-world physical testing and functional useFeatures:Excellent mechanical stiffnessElevated temperature resistanceDimensionally stableEasy-.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 355 °F | ASTM D648 |
| Polymer Resources PC/TP-GP3-G20 PC/Polyester Alloy, 20% Glass Reinforced Superior Chemical Resistance, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific) LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP OL004 PPS - Linear LNP* LUBRICOMP* OL004 is a compound based on PPS - Linear resin containing 20% PTFE. Added features of this grade include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP WG003 PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WG003 is a compound based on Polybutylene Terephalate resin cantain Graphite. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 355 °F | ASTM D648 |
| Spartech Noryl® GTX SP-52Z1 Structural Sheet Description: Structural SheetNoryl is a registered trademark of General Electric Company.Information provided by Spartech. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C @Thickness 3.20 mm |
354 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_NC3508 PPE+HIPS (Europe-Africa-Middle East) PRELIMINARY DATA. LNP* Stat-kon* Noryl_NC3508 compound is a 33% glass/mineral/carbon filled PPE+PS. ESD, high heat, tight tolerance: electronic packaging/chip trays. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp PK0049 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PK0049 is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include; Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C @Thickness 6.40 mm |
354 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX626 PPE+PS+PA Blowmolding and extrusion. High heat and chemical resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Eurostar Starflam P10003 PA6, Mineral Filled, Flame Retardant, Extrusion Starflam P10003 is a Mineral Filled, Halogen Free, Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Eurostar Starflam PK0049 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0049 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | |
| Covestro Makroblend® UT-640 G Polycarbonate + Polyester Blend Key Features:Contains FillerHigh impact or high impact modifiedLight stabilized or stable to lightSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.As of 1 Septembe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| 3D Systems DuraForm® GF Glass Filled Nylon For use with all selective laser sintering (SLS®) systems.ApplicationsHousings and enclosuresConsumer sporting goodsAppropriate for low- to mid-volume rapid manufacturingParts requiring machining o.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| ALM PA 250 Nylon 12 SLS Prototyping Polymer Highly Recyclable Nylon 12 Laser Sintering Material.Engineered for excellent mechanical properties, part definition and surface finish. Stabilized against thermal degradation resulting in little or.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| Ashley Polymers Ashlene® 630 Nylon 6, General Purpose A general purpose Nylon 6 resin for injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 114 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| A. Schulman ComAlloy Aqualoy® 143 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. In Aqualoy® materials, carefully selected base resins and proprietary additives meld hydrolytic stability an.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| ALM PA-615-GS Filled Nylon 12 Prototyping Polymer 50% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.Drop-in replacement for other commercially .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| E-Polymers TEKAMID® JN100 PPE+PA66 Filler Reinforced PA/PPE Alloy Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/P.. |
|||