ALM PA-615-GS Filled Nylon 12 Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | ALM Advanced Laser Materials |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ALM PA-615-GS Filled Nylon 12 Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.Drop-in replacement for other commercially available 50% glass sphere filled PA 12 laser sintering powders.PA 615 is more recyclable, produces a better part surface finish, and the dry powder flow has been optimized.Information provided by Advanced Laser Materials (ALM).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.670 g/cc | 0.0242 lb/in³ | ASTM D1895 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | Sintered; ASTM D792 |
| Particle Size | 50 µm | 50 µm | D50 |
| 35 - 100 µm | 35 - 100 µm | D10-D90 | |
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 235 °C |
50 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | XY; ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | XY; ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | XY; ASTM D638 |
| Flexural Modulus | 3.10 GPa | 450 ksi | XY; ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 186 °C | 367 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | 50% RH, 500V; ASTM D257 |
| Surface Resistance | 2.30e+14 ohm | 2.30e+14 ohm | 50% RH, 500V; ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
Users viewing this material also viewed the following:
- Hexion Bakelite™ PF 14694 Phenolic Formaldehyde Resin, High Surface Quality (discontinued **)
- H.C. Starck Pure Molybdenum ABL, Arc-Cast, Low Carbon Bar
- SABIC Innovative Plastics ULTEM 4211 PEI
- Techmer ES Electrablend® POM CF15 15% Carbon Filled
- UCAR Carbon UCAR® ATR Isostatic Molded Graphite
- Dow Corning MOLYKOTE® G-0103 GREASE
- Chosun Refractories HACT-170 High Alumina Castables
- 3M 2E93-EZ Protective Carpet Tapes
- Hexion Bakelite™ PF 7595 Phenolic Formaldehyde Resin, Low Coefficient of Friction, Galvanized, Conductive (di
Copyright © lookpolymers.com All Rights Reserved