Polymer Property : Flexural Strength = 152 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	152 MPa @Temperature 23.0 °C	22000 psi @Temperature 73.4 °F	ASTM D790
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) (Unverified Data**) Torlon 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500â€
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP600 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062"..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP602 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage, less than 250 volts, electrical applications.Thickne..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP605 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operatio..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP611 Paper Base Laminate Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" a..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP629 Paper Base Laminate Description: It is a paper-phenolic high-pressure laminate. It is intended primarily for mechanical applications and is suitable for electrical applications as well. Thickness Tested: 0.062", 0.125"..
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500"
Flexural Strength	152 MPa @Temperature 23.0 Â°C	22000 psi @Temperature 73.4 Â°F	ASTM D790
Solvay Specialty Polymers TorlonÂ® 4435 Polyamide-imide (PAI) TorlonÂ® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not ..
Flexural Strength	152 MPa @Temperature -40.0 °C	22000 psi @Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
Toyobo GLAMIDE® NB-5620S Nylon/Olefin GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..