Industrial Laminates/Norplex NP605 Paper Base Laminate

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP605 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operation. However, it is also used in other industries for tooling stock because of its ease of machining and good dimensional stability.Thickness Tested: 0.062", 0.125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.30 - 1.35 g/cc

@Thickness 1.57 mm
1.30 - 1.35 g/cc

@Thickness 0.0620 in
ASTM D792
Moisture Absorption at Equilibrium 8.0 %

@Thickness 1.57 mm
8.0 %

@Thickness 0.0620 in
ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80 - 100

@Thickness 1.57 mm
80 - 100

@Thickness 0.0620 in
ASTM D785
Tensile Strength, Yield 89.6 MPa

@Thickness 1.57 mm
13000 psi

@Thickness 0.0620 in
CW; ASTM D638
117 MPa

@Thickness 1.57 mm
17000 psi

@Thickness 0.0620 in
LW; ASTM D638
Flexural Strength 152 MPa

@Thickness 1.57 mm
22000 psi

@Thickness 0.0620 in
CW; ASTM D790
172 MPa

@Thickness 1.57 mm
25000 psi

@Thickness 0.0620 in
LW; ASTM D790
Compressive Strength 241 MPa

@Thickness 12.7 mm
35000 psi

@Thickness 0.500 in
ASTM D695
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Breakdown 60000 V

@Thickness 1.57 mm
60000 V

@Thickness 0.0620 in
Cond A; ASTM D229 S/S
Descriptive Properties Value Comments
Color Natural
Users viewing this material also viewed the following: